Ohmalloy 4j29 Strip 0.15mm*20mm for Stamping Shell Metal Ceramic

Product Details
Customization: Available
Product Type: Strip
Material: Fenico Alloy
Gold Member Since 2012

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

to see all verified strength labels (6)
Find Similar Products

Basic Info.

Model NO.
4j29
PCD
0~100
ET
0~100
Hole
0
Thickness
0.05~5mm
Condition
Bright Surface, Soft
Width
10~250mm
Heat Treatment
Done
Weight Coil
10~50 Kg
Transport Package
Coil+ Waterproof Paper+ Wooden Case
Trademark
Ohmalloy-4J29
HS Code
722699900
Production Capacity
5000 Kgs Per Month

Product Description

OhmAlloy-4J29  (Expansion alloy)

(Common Name: Kovar, Nilo K, KV-1, Dilver Po, Vacon 12)
OhmAlloy-4J29 also known as Kovar alloy. it was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
(-Kovar)
Kovar  is a nickel-cobalt ferrous alloy compositionally identical to Fernico, designed to be compatible with the thermal expansion characteristics of borosilicate glass (~5 × 10?6 /K between 30 and 200 °C, to ~10 × 10?6 /K at 800 °C) in order to allow direct mechanical connections over a range of temperatures. It finds application in electroplated conductors entering glass envelopes of electronic parts such as vacuum tubes (valves), X-ray and microwave tubes and some lightbulbs.
The name Kovar is often used as a general term for Fe-Ni alloys with these particular thermal expansion properties. Note the related particular Fe-Ni alloy Invar which exhibits minimum thermal expansion.
 
OhmAlloy-4J29was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
 
OhmAlloy-4J29 not only has thermal expansion similar to glass, but its nonlinear thermal expansion curve can often be made to match a glass, thus allowing the joint to tolerate a wide temperature range. Chemically, it bonds to glass via the intermediate oxide layer of nickel oxide and cobalt oxide; the proportion of iron oxide is low due to its reduction with cobalt. The bond strength is highly dependent on the oxide layer thickness and character. The presence of cobalt makes the oxide layer easier to melt and dissolve in the molten glass. A grey, grey-blue or grey-brown color indicates a good seal. A metallic color indicates lack of oxide, while black color indicates overly oxidized metal, in both cases leading to a weak joint.
 
Mainly used in electric vacuum components and emission control, shock tube, igniting tube, glass magnetron, transistors, seal plug, relay, integrated circuits lead, chassis, brackets and other housing sealing.
 
Normal composition%

Ni
28.5~29.5 Fe Bal. Co 16.8~17.8 Si ≤0.3
Mo ≤0.2 Cu ≤0.2 Cr ≤0.2 Mn ≤0.5
C ≤0.03 P ≤0.02 S ≤0.02    
 
Tensile Strength, MPa

Code of condition
Condition Wire Strip
R Soft ≤585 ≤570
1/4I 1/4 Hard 585~725 520~630
1/2I 1/2 Hard 655~795 590~700
3/4I 3/4 Hard 725~860 600~770
I Hard ≥850 ≥700
 
Typical Physical properties

Density (g/cm3)
8.2
Electrical resistivity at 20ºC(mm2/m) 0.48
Temperature factor of resistivity(20ºC~100ºC)X10-5/ºC 3.7~3.9
Curie point   Tc/ ºC 430
Elastic Modulus,  E/ Gpa 138
 
Coefficient of expansion
θ/ºC α1/10-6ºC-1 θ/ºC α1/10-6ºC-1
20~60 7.8 20~500 6.2
20~100 6.4 20~550 7.1
20~200 5.9 20~600 7.8
20~300 5.3 20~700 9.2
20~400 5.1 20~800 10.2
20~450 5.3 20~900 11.4

Thermal conductivity
θ/ºC 100 200 300 400 500
λ/ W/(m*ºC) 20.6 21.5 22.7 23.7 25.4
 
The heat treatment process
Annealing for stress relief Heated to 470~540ºC and hold 1~2 h. Cold down
annealing In vacuum heated to 750~900ºC
Holding time   14 min~1h.
Cooling rate No more than  10 ºC/min cooled to 200 ºC
 
Style of supply
Alloys Name Type Dimension  
OhmAlloy-4J29 Wire D= 0.1~8mm  
OhmAlloy-4J29 Strip W= 5~250mm T= 0.1mm
OhmAlloy-4J29 Foil W= 10~100mm T= 0.01~0.1
OhmAlloy-4J29 Bar Dia= 8~100mm L= 50~1000
         


Ohmalloy 4j29 Strip 0.15mm*20mm for Stamping Shell Metal Ceramic
Test Equipments
Ohmalloy 4j29 Strip 0.15mm*20mm for Stamping Shell Metal Ceramic

Ohmalloy 4j29 Strip 0.15mm*20mm for Stamping Shell Metal Ceramic

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier