| Product Type: | Wire |
|---|---|
| Resistivity(μΩ.Cm): | 8.44 |
| Electrical Resistivity at 20º: | 0.47c (Ωmm2/M) |
| Emf Vs Cu(μV/ºC )(0~100ºC ): | 1 |
| Melting Point (ºC): | 960 |
| Tensile Strength: | 390MPa |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Normal Manganin 47(Precision Resistance Alloy)
(Common Name:Normal Manganin,Normal Manganin 47,CuMn12Ni2 )
Normal Manganina 47 is a copper-manganese-nickel alloy (CuMnNi alloy) for use at room temperature. The alloy is characterized by very low thermal electromotive force (emf) compared to copper.
Normal Manganina 47 is typically used for the manufacturing of resistance standards, precision wire wound resistors, potentiometers, shunts and other electrical and electronic components.
Normal Manganin 47 widely used for precision resistors with the highest requirements, the resistors should be carefully stabilised and the application temperature should not exceed +60 °C. Exceeding the maximum working temperature in air may result in a resistance drift generated by oxidizing. Thus, the long-term stability can be affected negatively. As a result, the resistivity as well as the temperature coefficient of the electric resistance may slightly change.
It is also used as low cost replacement material for silver solder for hard metal mounting.The alloy's low emf vs. copper makes it ideal for use in electrical circuits, especially D.C., where a spurious thermal emf could cause malfunctioning of electronic equipment. Due to the low operating temperature, the temperature coefficient of resistance is controlled to be low over a range of 15 to 35°C .
Precision resistors
| Nickel | 2~3 | Manganese | 11~13 |
| Copper | Bal. |
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 180 | 390 | 15 |
| Density (g/cm3) | 8.44 |
| Electrical resistivity at 20ºC (Ωmm2/m) | 0.47 |
| Temperature factor of resistivity(20ºC~600ºC)X10-5/ºC | -3~20 |
| Conductivity coefficient at 20ºC (WmK) | 40 |
| EMF vs Cu(μV/ºC )(0~100ºC ) | 1 |
| Coefficient of thermal expansion | |
| Temperature | Thermal Expansion x10-6/K |
| 20 ºC- 400ºC | 18 |
| Specific heat capacity | |
| Temperature | 20ºC |
| J/gK | 0.41 |
| Melting point (ºC) | 960 |
| Element working temperature in air (ºC) | 5~45 |
| Magnetic properties | non-magnetic |
Corrosion resistance performance
| Alloys | Working In atmosphere at 20ºC | Working at max temperature 200ºC | |||||
|
Air and oxygen contain gases |
gases with Nitrogen |
gases with sulfur oxidability |
gases with sulfur reductibility |
carburization | |||
| Manganin 47 | good | good | good | good | bad | good | |
Style of supply
| Alloys Name | Type | Dimension | ||
| Manganin 47W | Wire | D=0.03mm~8mm | ||
| Manganin 47R | Ribbon | W=0.4~40 | T=0.03~2.9mm | |
| Manganin 47S | Strip | W=8~200mm | T=0.1~3.0 | |
| Manganin 47F | Foil | W=6~120mm | T=0.003~0.1 | |
| Manganin 47B | Bar | Dia=8~100mm | L=50~1000 | |