Audited Supplier Monel400 is the corrosion-resistant alloy with the largest amount, the most versatile and excellent comprehensive performance. The alloy has excellent corrosion resistance in hydrofluoric acid and fluorine gas media, and excellent corrosion resistance to hot concentrated alkali liquor. It is also resistant to corrosion by neutral solutions, water, sea water, atmosphere, organic compounds, etc. An important feature of this alloy is that stress corrosion cracking is generally not produced and the cutting performance is good.
Monel 400 Chemical composition
Alloy |
% | Ni | Cu | Fe | C | Mn | Si | S |
| Monel400 | Min. | 63 | 28 | |||||
| Max. | 34 | 2.5 | 0.3 | 2 | 0.5 | 0.024 |
Monel 400 Physical properties
| Density | 8.83 g/cm³ |
| Melting point | 1300-1390 °C |
Monel 400 Alloy minimum mechanical properties in the room temperature
Alloy state |
Tensile strength Rm N/mm² |
Yield strength R P0. 2 N/mm² |
Elongation A 5 % |
| Monel400 | 480 | 170 | 35 |
Mechanical character
| Shape | Tensile strength |
Yield strength (0.2% offset) |
Elongation% | Hardness | |||
| KSI | MPa | KSI | MPa |
Brinell (3000-kg) |
Rockwell B | ||
| Bar | 70-110 | 480-760 | 25-85 | 170-185 | 5-50 | 110min | 60min |
| Plate | 70-95 | 482-655 | 28-75 | 193-517 | 30-50 | 110-215 | 60-96 |
| Sheet | 70-120 | 482-827 | 30-110 | 207-758 | 2-42 | - | 65min |
| Strip | 70-140 | 482-965 | 25-130 | 172-896 | 2-50 | - | 68min |
| Tube | 70-130 | 482-896 | 25-110 | 172-758 | 3-50 | - | 100max |
| Wire | 70-180 | 482-1241 | 30-170 | 207-1172 | 2-45 | - | |
Specification
| Monel Form | Size |
| Monel Spring wire | 0.08mm-10mm |
| Monel plate | 0.3mm-15mmX1000mmX L |
| Monel strip | 0.06mm-2.0mmX 200mm X L |
| Monel Rod | 8mm-40mm X L |
| Monel welding wire | 1.2mm, 1.6mm, 2.0mm |
Characteristic as below
1.Monel 400 Metallurgical structure
2.Monel 400 alloy is high-intensity single-phase solid solution.
3, chloride ion stress corrosion cracking is very insensitive;
4. Excellent mechanical performance from below zero to 550ºC;
5. It can be used as pressure vessel under -10~425ºC as approved by ASME;
6. Good machining and welding performance
7.Good corrosion resistance in Marine and chemical environment;
Gas Corrosion:Monel 400 alloys have excellent corrosion resistance in fluorine, hydrochloric acid, sulfuric acid, hydrofluoric acid and their derivatives. At the same time, it is more resistant to corrosion in seawater than copper-based alloys.
Acid medium: Monel 400 is corrosion resistant in sulfuric acid with a concentration of less than 85%. Monel400 is one of the few materials that are resistant to hydrofluoric acid.
Water corrosion: Monel400 alloy has excellent corrosion resistance in most water corrosion conditions, and pitting corrosion and stress corrosion are rarely found. The corrosion rate is less than 0.025mm/a.
High temperature corrosion: The maximum temperature of Monel400 working continuously in air is generally around 600 °C. In high temperature steam, the corrosion rate is less than 0.026 mm/a.
Ammonia: Due to its high nickel content, Monel400 alloy can withstand corrosion under anhydrous ammonia and ammoniating conditions below 585 °C.
Monel 400 Application field
Monel 400 alloy is a multi-purpose material in many industrial applications:
1. Seamless water pipe in the power factory
2. Sea-water exchanger and evaporator
3. Sulfuric acid and hydrochloric acid environment
4. Crude distillation
5. Sea-water in the use of equipment and propeller shaft
6. Nuclear industry and used in the manufacture of uranium enrichment isotope separation equipment
7. Manufacturing hydrochloric acid equipment used in the production of pump and valve