Magnetic Temperature Compensation Element Be Made by Feni50 Alloy

• Customization: Available
• Smelting Type: Vacuum Melting
• Granularity: 0
• Usage: Industrial
• Type: Feni Alloy
• Shape: Strip
• Density (g/cm3): 8.2
• Curie Point: 500
• Surface: Bright
• Condition: Annealing
• Electrical Resistivity: 0.45
• Transport Package: Wooden Case
• Specification: 0.5 mm
• Trademark: Ohmalloy
• Origin: China
• HS Code: 7226999001
• Production Capacity: 10000 Kg Per Month

Product Description

OhmAlloy-1J50  (Soft magnetic alloy)
(Common Name: Ni50, E11a, 50H, Hy-Ra49, PB)

Ohmalloy-1J50 is a nickel-iron magnetic alloy, with about 50% nickel and 48% iron content. It is derived in accordance with permalloy. It has characteristics of high permeability and high saturation magnetic flux density.
Alloy melting in a vacuum medium, cast into ingots, after hot forging blanks made of sheet metal, and then after hot rolling, pickling, surface treatment, cold rolling into finished products.
Ohmalloy-1J50 Iron-nickel alloy( soft magnetic alloy) mostly in an alternating magnetic field used mainly for high magnetic yoke, sensitive relays, low-loss micro-motor, small power transformers, pulse transformer, transistor switches, magnetic amplifier magnetic modulator, sensitive signal input and output transformers, magnetic heading aviation instrumentation magnetic sensor, magnetic susceptibility measurement instrument components, precision meter movable piece and the stator magnetic shielding and magnetic temperature compensation element.
 

Normal composition%

Ni	49.0~51.0	Fe	Bal.	Mn	0.3~0.6	Si	0.15~0.3
Mo	-	Cu	≤0.2
C	≤0.03	P	≤0.02	S	≤0.02

 

Typical Mechanical properties

Yield strength	Tensile Strength	Elongation
Mpa	Mpa	%
685	780	3~35

 

Typical Physical properties

Density (g/cm3)	8.2
Electrical resistivity at 20ºC(Om*mm^2/m)	0.45
Coefficient of linear expansion(20ºC~200ºC)X10^-6/ºC	9,2
Saturation magnetostriction coefficient λθ/ 10^-6	25,0
Curie point   Tc/ ºC	500

 

The magnetic properties of alloys with high permeability in weak fields
1J50	Initial permeability	Maximum permeability			Coercivity	Saturation magnetic induction intensity
Сold-rolled strip/ sheet. Thickness, mm	μ0.08/ (mH/m)		μm/ (mH/m)	Hc/ (A/m)			BS/ T
	≥			≤
0.05 mm	2.5		35	20			1.5
0.1~0.19 mm	3.8		43.8	12
0.2~0.34 mm	4.4		56.3	10.4
0.35~1.0 mm	5.0		65	8.8
1.1~2.5 mm	3.8		44.0	12
Bar
8-100 mm	3.1		25.0	24

 

Mode of heat treatment  1J50
Annealing media	Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 ºC.
The heating temperature and rate	1100~1150ºC
Holding time/h	3~6
Cooling rate	With 100 ~ 200 ºC/ h cooled to 600 ºC, Rapid cooling to 300 baked

Style of supply

Alloys Name	Type	Dimension
OhmAlloy-1J85	Wire	D= 0.1~8mm
OhmAlloy-1J85	Strip	W= 8~390mm	T= 0.3mm
OhmAlloy-1J85	Foil	W= 10~100mm	T= 0.01~0.1
OhmAlloy-1J85	Bar	Dia= 8~100mm	L= 50~1000